Austenitic precipitation hardening Stainless Steel Alloy 630 Plate retain their austenitic structure after annealing and hardening by ageing. At the annealing temperature of 1095 to 1120°C the precipitation hardening Stainless Steel Alloy 630 Plate part is soluble. Hardness remains Stainless Steel Alloy 630 Plate lower than that for martensitic or semi-austenitic precipitation hardening steels.
Stainless Steel Alloy 630 Plate Mechanical Properties
Condition | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness | |
Rockwell C (HR C) | Brinell (HB) | ||||
Solution Treated | 1105 typ | 1000 typ | 15 typ | 38 max | 363 max |
Condition 900 | 1310 min | 1170 min | 10 min | 40 min | 388 min |
Condition 1150 | 930 min | 724 min | 16 min | 28 min | 277 min |
Products partially or completely constructed of 17-4 PH include:
Air spray guns
Bearings
Boat fittings
Castings
Dental components
Fasteners
Gears